Description
TACKSOL 10/89 HSC is a solvent-borne pressure sensitive adhesive, based on natural rubber and special resins. After curing, it develops a very good resistance to ageing and heat.
Application
TACKSOL 10/89 HSC can be applied on any substrate (paper, PET, PP, PE, PVC,...).
If TACKSOL 10/89 HSC is applied on PVC, it is necessary to use a suitable primer, whereas it can be applied directly on other substrates.
This product is recommended for the production of protective films and tapes used on rough surfaces.
Technical Specifications
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 1 | Total Solids | % | 30±1 |
| 3 | Brookfield Viscosity 25°C | mPa.s | 1000 - 20001 |
| Solvents | hexane | ||
| Notes | |||
| 1 | N. 2 RV; 20 RPM | ||
Film properties
| Method of analysis | MU | Standard | |
|---|---|---|---|
| 11 | Peel Adhesion on Steel | g/in | 1,800 |
| 17 | Rolling Ball Tack | cm | 4 |
| 97 | Loop Tack Test | g | 2,200 |
| Average values; 22±2 g/m² of dry adhesive on PET film 36 µm | |||
Handling
For protective tapes it is necessary to cure the product with isocyanate (e.g. CURING AGENT D), in this case the pot-life of the adhesive is reduced as crosslinking starts immediately after the addition of the curing agent. The amount of isocyanate depends on the final requested characteristics.
Packaging
The product is supplied in iron drums (145 kg).
Storing
Store at temperature not higher than + 40°C, protected from heat sources and direct sunlight. Keep containers well closed, to prevent solvent evaporation. In case of prolonged storage, stir well before use.
Use within 12 months from production date (unopened and in the original packaging).
| Mod. DT3002E | Creation date: 1/18/2016 | Revision: 3 | Revision date: 14 Feb 2017 |
Above information is reliable, but does not constitute warranty.